Posts
1,077 -
Joined
-
Last visited
-
Days Won
8
Content Type
Profiles
Forums
Blogs
Gallery
Downloads
Events
Everything posted by Lord_James
-
https://warthunder.com/en/news/6863-development-shimakaze-fast-as-the-wind-en tl;dr, Shima has only 2x 12.7cm turrets in the style of a late war Kagero, as well as some other issues...
-
Nanostructured steel plates.
Lord_James replied to Militarysta's topic in Ballistics Science Discussion
Do you have any recommendations or authors? -
What turret is this? It looks a little too square to be a ZSU-57, but the size is about right.
- 1,589 replies
-
Looks like the projectile came in at an angle, considering the gouging on one side. Could the projectile have been a 14.5mm or maybe a 20mm SLAP?
-
Ah shit, I totally forgot to tell you all how my JPA armor from the previous competition was made: basically it is a pseudo lamination of a FHA plate (hardened as deep as possible) with an additional RHA plate, as thick as the backing layer of the FHA, placed onto the hardened side. The process involves taking the FHA, and then hydraulically pressing it into a fresh, red hot RHA "box" (that is slightly convex) and holding it there until the RHA is able to weld (if not using hot welding). The hardened face being pressed into is suppose to be rough, to give more surface area for the outer box to bond. The box sides are suppose to be long enough to come close to the back of the FH plate, where the more ductile (and easily weldable) section is, and welded back there, entombing the FH section and creating an armor package. When mounting in a vehicle, the "box" RHA layer is suppose to be the farthest from the inside, so that it is the first layer struck in the package. As an example, if I have a 100mm plate hardened 25mm through, there would be a 75mm "box" place on it's face, and would produce a full 175mm package (the side tabs that are welded to the rear of the plate do not have to be 75mm thick). I intended for this armor to be the base armor due to it being expensive and time consuming to make, but used as such would probably be exceptional at it's job due to it almost exclusively having to defeat damaged penetrators and disrupted HEAT jets. Hope you guys are inspired by this in the next competition, might be useful for enhancing the armor protection of such a light vehicle.
- 85 replies
-
- competition
- armored car
-
(and 3 more)
Tagged with:
-
https://warthunder.com/en/news/6830-development-new-t-72-modifications-here-come-the-top-of-the-line-russians-en More T-72s FTW, also the comments are great, glad i left that train wreck before it actually fell apart
-
The Soviet Tank Thread: Transversely Mounted 1000hp Engines
Lord_James replied to T___A's topic in Mechanized Warfare
cross posting this, because it is Russian tank, and it has the new T-72 UBKH, @LoooSeR's fAVoRitE! https://warthunder.com/en/news/6830-development-new-t-72-modifications-here-come-the-top-of-the-line-russians-en- 5,188 replies
-
- soviet
- russian bias
-
(and 15 more)
Tagged with:
- soviet
- russian bias
- kharkovites get out
- kotin number 1 diva of ages
- kartsev did nothing wrong
- reminder that the is-7 had 8 machine guns
- reminder that uvz built more t-34s than khpz
- real life has a uvz bias
- make lkz great again
- t-72 over t-64 all day erry day
- t-80 worst mistake of lkz life
- the object 167t engine was better
- so was object 278 engine
- t-64 so weak it cannot handle glorious t-34 engine which conquered hitlerite germany
- t-64
- t-72
- heavy tanks
-
BlackTailDefense Doesn't Know Shit About Tank Design
Lord_James replied to Collimatrix's topic in Mechanized Warfare
I am in physical pain- 123 replies
-
- military reform
- tanks
- (and 4 more)
-
BlackTailDefense Doesn't Know Shit About Tank Design
Lord_James replied to Collimatrix's topic in Mechanized Warfare
Hmmm, “The tanks ammo is extremely large and heavy... and would probably break an autoloader” 1. And the proposed ammunition wouldn’t also break the backs of the poor SoaB(s) having to load this gun? 2. I’m just going to refer you to any ship with large caliber guns, which almost exclusively used loading assistance*, but most importantly, the 8 inch Mark 16 used on the Des Moines class, and the 6 inch Mark 16 on the Worcester. *Warships also have a couple other problems that required machines like ammunition elevators and rammers, that the small scale of tanks don’t have to worry about.- 123 replies
-
- military reform
- tanks
- (and 4 more)
-
Collimatrix's Terrible Music Thread
Lord_James replied to Collimatrix's topic in Fiction & Entertainment
Not bad- 904 replies
-
- music
- stuff white people like
-
(and 1 more)
Tagged with:
-
The interesting ship photos/art thread.
Lord_James replied to Belesarius's topic in Naval Discussion
https://www.history.navy.mil/our-collections/photography/numerical-list-of-images/nhhc-series/s-file/S-584-110.html An 80,000 ton battleship proposal, meant to be the maximum size that could still use the Panama Canal. this one in particular is my favorite out of all the 80,000 ton proposals because she is armed with sextuple, 16 inch turrets, for a broadside of 24 shells, or 3 times that of the Colorado class (or all 3 Colorado’s combined). Also has 18 inch belt armor and a claimed maximum speed of 25 knots. -
Hmmmm, for them to gain experience points to upgrade their virtual tanks, they would have to play mostly the online multiplayer... which is certainly how real life warfare is fought... *has flashbacks to kamikaze Ju-87s and Uber flanking, spawn camping light tanks*
-
I know this says WoT and WT, but would this also include World of Warships (WoWs), since several people have posted about world of warplanes?
-
GOTTA GO FAST (Speedrunning)
Lord_James replied to Oedipus Wreckx-n-Effect's topic in Fiction & Entertainment
They’ve started to get below 3 hours in 100% Eternal runs 2 hours, 17 minutes for Doom 2016, as well -
Collimatrix's Terrible Music Thread
Lord_James replied to Collimatrix's topic in Fiction & Entertainment
Another pretty good metal soundtrack, some of my favorites being “Inferno” (4:21), “Devil”, and “Phobos Anomaly”. Names and times of specific tracks are in the description of the video. Also, some of Mick Gordon’s previous work:- 904 replies
-
- music
- stuff white people like
-
(and 1 more)
Tagged with:
-
Collimatrix's Terrible Music Thread
Lord_James replied to Collimatrix's topic in Fiction & Entertainment
I guess I’ll say it: it’s not as good as the 2016 soundtrack. None of the tracks really stand out to me, unlike the original’s “Rip and Tear” “Damnation” “BFG Division” or even the short “At Doom’s Gate”. A lot of the notes used also sound a little to electronic/synthetic, and the base is notably reduced. Also, this soundtrack starts with what could be considered ambiance music, unlike 2016’s opening being a short monologue and then directly into some of the best metal I’ve ever heard.- 904 replies
-
- music
- stuff white people like
-
(and 1 more)
Tagged with:
-
Saudi Arabia to begin operations in Yemen
Lord_James replied to Priory_of_Sion's topic in Open Discussion
Saudi AF is too busy bombing schools and hospitals to attack the Houthis -
Was about to ask the same question about size limit. Now, I do remember that Mowag made a 10x10 version of the Piranha once, might go with something like that. There is only the 30mm auto cannon and the RRs? No larger auto cannons or artillery / field guns?
- 85 replies
-
- competition
- armored car
-
(and 3 more)
Tagged with:
-
What is “I^2 - Gen 2” under electronics?
- 85 replies
-
- competition
- armored car
-
(and 3 more)
Tagged with:
-
General artillery, SPGs, MLRS and long range ATGMs thread.
Lord_James replied to LoooSeR's topic in Mechanized Warfare
railway guns making a comeback I see- 1,903 replies
-
Conversely, if you’re looking for something more empirical to base your judgments on, you can calculate the energy each bullet has within that range; more energy would imply more penetration for dealing with body armors and punching through make-shift fortifications like stone/concrete, though this is not always the case.
-
Nanostructured steel plates.
Lord_James replied to Militarysta's topic in Ballistics Science Discussion
After getting some time to read through the article provided by @Militarysta (thank you), I can sorta see how they can pull it off: Manganese and Silicon are both great for making strong steel, manganese increasing the harden-ability of low carbon steels, and silicon also increasing the harden-ability, and having the added benefit of maintaining the harness after tempering. http://navweaps.com/index_nathan/metalprpsept2009.php#Manganese http://navweaps.com/index_nathan/metalprpsept2009.php#Silicon The retention of the bainite is still a mystery to me, as tempering and annealing (as discussed in the article) would transform the bainite with the remaining austenite into a more stable structure (again, pearlite), though maybe the large amount of silicon present (1.56-1.61% by mass) is interfering? I’m curious too see how this armor develops, if they can make the plates thicker, or if they can keep the quality control while making these plates on a full industrial level. -
Nanostructured steel plates.
Lord_James replied to Militarysta's topic in Ballistics Science Discussion
Huh, that’s weird, usually Bainite is undesired for armor or structural components due to excessive brittleness: http://navweaps.com/index_nathan/metalprpsept2009.php#Bainite pearlite being just as tough but less brittle (on average) and martensite also being less brittle, and even tougher. Unless they want the contents of the container to fall out after the first hit, like ERA or something similar, this doesn’t look like an advancement.